Aluminum-free borosilicate glass and applications thereof

ABSTRACT

The aluminum-free borosilicate glass has a composition in percent by weight based on oxide content of: SiO 2 , 65-77; B 2 O 3 , 7-20; Li 2 O, 0-2; Na 2 O, 0-4; K 2 O, 3-12; MgO, 0-2; CaO, 0-2; with MgO+CaO, 0-3; BaO, 0-3; ZnO, 0-2; ZrO 2 , 0.8-12; TiO 2 , 0-10; CeO 2 , 0-1; and F − , 0-0.6. This glass advantageously has a coefficient of thermal expansion α (20° C.; 300° C.) of between 3.0×10 −6 /K and 6×10 −6 /K, good chemical resistance and a working point V A  of between 990° C. and 1290° C.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates to borosilicate glass and also to uses of the glass.

[0003] 2. Description of the Related Art

[0004] The group of the borosilicate glasses is extremely extensive. The representatives of this group have the following basic composition range in common:

[0005] SiO₂, approx. 70 to 80 percent by weight,

[0006] B₂O₃, 7 to 20 percent by weight,

[0007] Al₂O₃, 2 to 7 percent by weight,

[0008] Alkali metal oxides, 3 to 10 percent by weight.

[0009] The glasses contain aluminum oxide in order to improve their resistance to devitrification and the chemical resistance.

[0010] However, glasses of this type release aluminum ions to a wetting aqueous liquid, which is disadvantageous for certain applications. For example, aluminum is currently suspected of harming the health of people of corresponding disposition. In such cases, therefore, conventional primary pharmaceutical packaging materials made from glass are relatively unsuitable for the administration of injectable substances.

[0011] Furthermore, aluminum oxide increases the melting and working points of the glasses considerably, increasing the energy consumption involved in the production processes.

[0012] The physical and glass-technical properties influenced by Al₂O₃ generally cannot be reproduced by simply replacing the aluminum oxide with one or more other constituents. Rather, completely new developments or extensive changes to the glass composition are required.

[0013] Standard borosilicate glasses are distinguished by their high chemical stability and their high ability to withstand temperature changes. They have a low coefficient of thermal expansion.

[0014] On account of these properties, they are used in particular as ampoules and vials in the pharmaceutical industry for packaging, for example, injection preparations, for apparatus and equipment used in the chemical industry, both in production and on a laboratory scale, or as lamp glasses.

[0015] There is extensive patent literature concerning glasses of this type.

[0016] For example, DE 42 30 607 C1 describes chemically highly resistant borosilicate glasses which can be fused to tungsten. According to the examples, the glasses have working points V_(A)>1210° C.

[0017] The borosilicate glasses described in German Laid-Open Specification DE 37 22 130 A1 also have high working points. Although the glasses belong to the first hydrolytic glass, they are relatively susceptible to crystallization, on account of the absence of K₂O in these glasses.

[0018] The Li₂O-containing glasses described in German Patent DE 195 36 708 C1 are also highly chemically stable but also have disadvantageously high working points.

[0019] The glasses described in German Patent DE 44 30 710 C1 have a high SiO₂, content, namely >75 percent by weight and >83 percent by weight of SiO₂+B₂O₃ in combination with an SiO₂/B₂O₃ weight ratio of >8, which means that they are chemically highly stable but also have excessively high working points.

SUMMARY OF THE INVENTION

[0020] Therefore, it is an object of the invention to find a glass, which satisfies the above-mentioned requirements imposed on previous borosilicate glasses, has favorable working points and is free of Al₂O₃.

[0021] According to the invention the aluminum-free borosilicate glass has good chemical resistance and a composition, in percent by weight, based on oxide content, of: SiO₂ 60-78 B₂O₃  7-20 Li₂O 0-2 Na₂O 0-4 K₂O  3-12 MgO 0-2 CaO 0-2 with MgO + CaO 0-3 BaO 0-3 ZnO 0-2 ZrO₂ 0.8-12  TiO₂  0-10 CeO₂ 0-1 F⁻   0-0.6

[0022] and optionally at least one refining agent in a standard amount for refining.

[0023] The glass according to the invention has an SiO₂ content of at least 60, preferably at least 63% by weight, and at most 78% by weight, preferably of 65 to 77% by weight, especially of 67 to 75% by weight, particularly preferably of 68 to 74% by weight. The SiO₂ content varies according to the specific application of the glass and has an advantageous effect on the desired properties of high chemical resistance, in particular high acid resistance, and low coefficient of thermal expansion.

[0024] The glass contains 7-20% by weight, preferably 9 to 18% by weight, particularly preferably 9-13% by weight, of B₂O₃ in order to reduce the thermal expansion, the working point and the melting point while at the same time improving the chemical resistance, in particular the hydrolytic stability. The boric acid bonds the alkali metal ions which are present in the glass more firmly into the glass structure, which leads to a reduced release of alkali metal ions in contact with solutions, for example during the measurement of the hydrolytic stability. Whereas at low contents the hydrolytic stability would deteriorate significantly and the melting point would not be reduced far enough, at higher contents the acid resistance would deteriorate. Although levels of over 13% of B₂O₃ adversely affect the chemical resistance, for certain applications, such as lamp glass for electronic flashbulbs and backlights, they have the advantage that the high boric acid content additionally produces a higher electrical resistance of the glass.

[0025] Apart from inevitable impurities, the glass is free of Al₂O₃.

[0026] The individual alkali metal oxide contents within certain limits are important for the glass according to the invention, so that in particular the hydrolytic stability is improved compared to the specific prior art glass, which is intended for the corresponding use.

[0027] For example, the glass contains 0-4% by weight of Na₂O, preferably 0-3% by weight of Na₂O, 3-12% by weight of K₂O, preferably 5-10% by weight of K₂O, and 0-2% by weight of Li₂O, preferably 0-1% by weight of Li₂O. The sum of the alkali metal oxides is preferably between 5.5 and 13.5% by weight.

[0028] It is particularly preferable for Na₂O or Li₂O to be present in the glass in addition to K₂O. It is very particularly preferable for Na₂O and Li₂O to be present in the glass in addition to K₂O.

[0029] The alkali metal oxides reduce the working point of the glass, and moreover high K₂O contents improve the resistance to devitrification, a property that is of crucial importance in the Al₂O₃-free glass according to the invention. During the cooling, as part of the forming process, for example tube join, no devitrification crystals, which would remain at the glass surface and adversely affect the forming and use of the glass, are formed.

[0030] The release of alkali metal ions increases disproportionately above the respective upper limit of the alkali metal oxide. Conversely, the specific levels result in a minimum release of alkali metal ions, leading to the various excellent chemical resistances.

[0031] In a very particularly preferred embodiment, the glass contains at least 0.2% by weight of Li₂O. In a very particularly preferred embodiment, the glass contains at least 0.3% by weight of Na₂O, in particular at least 0.5% by weight of Na₂O.

[0032] As further components, the glass may contain the divalent oxides MgO in an amount of 0-2% by weight, CaO in an amount of 0-2% by weight, preferably 0-1% by weight, ZnO in an amount of 0-2% by weight and BaO in an amount of 0-3% by weight, preferably 0-1% by weight. These components vary the “length of the glass”, i.e. the temperature range within which the glass can be processed. The differing extent to which these components modify the network means that, by swapping between these oxides, it is possible to match the viscosity characteristics to the requirements of the particular production and working process. CaO and MgO reduce the working point and are securely bonded into the glass structure. The sum of CaO and MgO should be between 0 and 3% by weight, since at higher levels the thermal expansion increases. The addition of BaO makes it possible to reduce the working point without adversely affecting the hydrolytic stability of the glass.

[0033] It is preferable for the glass to be free of MgO, CaO, BaO and to contain between 0-1% by weight of ZnO. In particularly preferred embodiments, ZnO is also not present.

[0034] The glass contains 0.8-12% by weight of ZrO₂, preferably at most 10.5% by weight of ZrO₂, especially at least 1.5% by weight of ZrO₂, in particular at least 2% by weight of ZrO₂, particularly preferably 3-7% by weight of ZrO₂. ZrO₂ improves the hydrolytic stability and in particular the alkali resistance of the glass. At higher levels, the working point would be increased excessively without the chemical resistances being improved significantly any further.

[0035] The glass may contain up to 10% by weight, preferably up to 6% by weight, especially up to 5% by weight of TiO₂. Small amounts of up to 1% by weight of TiO₂ prevent solarization of the glass, the subsequent darkening of, for example, a lamp produced therefrom while it is operating, and also even improve the chemical resistance. Levels of over 1% by weight in particular improve the chemical resistance of the glass, e.g. the alkali resistance. A TiO₂ content of between 0 and 1% by weight is particularly preferred. In a particularly preferred embodiment, the glass is free of TiO₂. In another embodiment, the glass contains at least 0.5% by weight of TiO₂. TiO₂ in this case has UV-blocking action. A TiO₂ content of at least 4.5% by weight of TiO₂ is preferred.

[0036] The glass may contain up to 1% by weight of CeO₂. In low concentrations, CeO₂ acts as a refining agent, while in higher concentrations it prevents the glass from being discolored by radioactive radiation. Therefore, seals made using a CeO₂-containing glass of this type can still be visually checked for any damage, such as cracks or corrosion to the conductor wire, even after they have been subjected to radioactive exposure. A high transparency of the glass is also desirable when the glass is used as primary pharmaceutical packaging material, since the contents are checked for any particles, which may be present. Still higher CeO₂ concentrations make the glass more expensive and lead to an undesirable yellow-brownish coloration of the glass. For uses in which the ability to avoid discoloration caused by radioactive radiation is not crucial, a CeO₂ content of between 0 and 0.4% by weight is preferred. The glass may without problems contain up to 0.5% by weight of Fe₂O₃. It preferably contains 0-0.1% by weight of Fe₂O₃.

[0037] Furthermore, the glass may contain up to 0.6% by weight of F⁻. This reduces the viscosity of the melt, which accelerates the melting of the batch and the refining of the melt. Moreover, as the F content of the glass increases, the pH of an aqueous solution, which is in contact with the glass, is buffered. What this means is that the increase in the pH in the filling contents which results from the release of alkali metal ions from the inner surface of the glass after injectable substances have been introduced into glass vessels is partially neutralized by F⁻ ions.

[0038] The glass may, if appropriate, contain further refining agents in addition to the above-mentioned CeO₂ and fluorides, for example Na₂SiF₆. For example, it can be refined using standard refining agents, such as chlorides, for example NaCl, and/or sulfates, for example Na₂SO₄, which are to be found in standard quantities, i.e., depending on the quantity and type of refining agent used, in quantities of from 0.003 to 1% by weight, in the finished glass. If As₂O₃ and Sb₂O₃ are not used, the glasses are free of As₂O₃ and Sb₂O₃, apart from inevitable impurities, which is particularly advantageous for their use as primary pharmaceutical packaging material.

[0039] The glass according to the invention has a coefficient of thermal expansion α_(20/300) of between 3.0×10⁻⁶/K and 6×10⁻⁶/K, so that it can be successfully fused to materials with similar thermal expansion characteristics, for example to molybdenum, tungsten and Fe—Co—Ni alloys, for example KOVAR®.

[0040] The glass has a high ability to withstand temperature changes and a high ability to withstand thermal loads. The glass has very high chemical resistances, in particular a high hydrolytic stability and a high alkali resistance. The glass has a very high resistance to devitrification, meaning that it is also eminently suitable for hot-forming by means of tube join. It is eminently suitable for use as apparatus glass.

[0041] The glass has working points of between 990° C. and 1290° C. The glass has relatively low melting points, namely between approximately 1480° C. and approximately 1590° C.

[0042] The resulting favorable melting and working range reduces the energy consumption during production.

[0043] Apart from inevitable impurities, the glass is free of Al₂O₃.

[0044] With this range of properties, the glass is eminently suitable for a very wide range of uses, for example for use as primary pharmaceutical packaging material, such as ampoules or vials, since the substances stored in the containers, in particular aqueous solutions, do not significantly attack the glass, i.e. the glass does not release any ions or releases only a few ions, in particular does not release any aluminum ions.

[0045] The glass is eminently suitable as a sealing glass for glass-metal seals, for example for sealing to molybdenum, tungsten and KOVAR®.

[0046] The glass is eminently suitable as a lamp glass, particularly as a glass for electronic flashbulbs and for fluorescent lamps, in particular for miniaturized fluorescent lamps, known as backlights.

[0047] The glass is eminently suitable for processing to form glass fibers, in particular to form glass fibers for reinforcing concrete.

[0048] Various sub-ranges are particularly preferred within the composition range claimed. These sub-ranges are particularly suitable for specific application areas.

[0049] For example, an Al₂O₃-free borosilicate glass having the composition (in % by weight, based on oxide) SiO₂ 71-74, B₂O₃ 9-12, Li₂O 0-1, Na₂O 0-3, K₂O 7-10, with Li₂O+Na₂O+K₂O 7-13.5, ZrO₂ 4 to 7 and, if appropriate, standard refining agents in standard quantities for refining, is particularly preferred.

[0050] A glass of this type satisfies the requirements of resistance classes 1 both in terms of hydrolytic stability and in terms of acid and alkali resistance. It is particularly suitable for use as a primary pharmaceutical packaging material.

[0051] Furthermore, a glass having the composition (in % by weight, based on oxide) SiO₂ 68-71, B₂O₃ 8-11, Li₂O 0-1, Na₂O 0-3, K₂O 8-11, with Li₂O+Na₂O+K₂O 8-13.5, ZrO₂ 7.5-10.5 and, if appropriate, standard refining agents in standard quantities for refining, is particularly preferred.

[0052] This glass with a high ZrO₂ content likewise fulfils the requirements of classes 1 of the above-mentioned chemical resistances. Particularly on account of its excellent alkali resistance, it is especially suitable as a glass for glass fibers in concrete.

[0053] Furthermore, a glass belonging to the composition range (in % by weight, based on oxide) SiO₂ 70-75, B₂O₃ 15-18, Li₂O 0-1, Na₂O, 0-3, K₂O 5-8, with Li₂O+Na₂O+K₂O 5.5-10.5, CaO 0-1, BaO 0-1, TiO₂ 0-1, ZrO₂ 0.8-5 and, if appropriate, standard refining agents in standard quantities for refining, is particularly preferred.

[0054] On account of its coefficient of thermal expansion α(20° C.; 300° C.) of between 4.7×10⁻⁶/K and 5.3×10⁻⁶/K, it is particularly suitable as a sealing glass for sealing to tungsten.

[0055] A glass belonging to the composition range (in % by weight, based on oxide) SiO₂ 67-70, B₂O₃ 15-18, Li₂O 0-1, Na₂O 0-3, K₂O 7-10, with Li₂O+Na₂O+K₂O 7-12.5, ZnO 0-1, ZrO₂ 2.5-6 and, if appropriate, standard refining agents in standard quantities for refining, is also particularly preferred.

[0056] On account of its coefficient of thermal expansion α(20° C.; 300° C.) of between 4.7×10⁻⁶/K and 5.3×10⁻⁶/K, it is particularly suitable as a sealing glass for sealing to molybdenum and to KOVAR®.

[0057] The latter two groups are especially suitable for use as lamp glasses.

[0058] In particular on account of the high electrical resistance of the glasses, caused by the high B₂O₃ contents, they are particularly suitable for use as bulbs for electronic flashbulbs and for fluorescent lamps, in particular miniaturized fluorescent lamps.

[0059] Furthermore, a glass belonging to the composition range (in % by weight, based on oxide) SiO₂ 74-78, B₂O₃ 12-15, Li₂O 0-1, Na₂O 0-3, K₂O 3-8, with Li₂O+Na₂O+K₂O 3-11, ZnO 0-1, ZrO₂ 2.5-7 and, if appropriate, standard refining agents in standard quantities is particularly preferred. On account of its high chemical resistances and its low coefficient of thermal expansion, it is particularly suitable as glass for equipment and apparatus, in particular for laboratory and production areas in particular in the chemical industry.

EXAMPLES

[0060] Eleven examples of glasses according to the invention (A1-A11) and four Al₂O₃-containing comparative examples (V1-V4) were melted from standard raw materials.

[0061] Table I gives the respective compositions (in % by weight, based on oxide content) of the glasses and important properties of the glasses, namely the coefficient of thermal expansion α(20° C.; 300° C.) [10⁻⁶/K], the transformation temperature T_(g)[° C.], the softening point E_(W)[° C.], the working point V_(A)[° C.] and the hydrolytic stability, the acid resistance and the alkali resistance.

[0062] To document the blocking in the UV region, for examples A6-A11 the maximum wavelength at which the transmission τ<0.1% (for a specimen thickness of 0.2 mm) is given (“UV blocking”).

[0063] The chemical resistances were determined in the following way:

[0064] the hydrolytic stability H in accordance with DIN ISO 719. The table in each case indicates the base equivalent of the acid consumption as μg Na₂O/g of glass grit. The maximum value for a chemically highly resistant glass belonging to hydrolytic class 1 is 31 μg Na₂O/g. The maximum value for a glass belonging to hydrolytic class 2 is 62 μg Na₂O/g. The maximum value for hydrolytic class 3 is 264 μg Na₂O/g.

[0065] The acid resistance S in accordance with DIN 12116. The table in each case indicates the weight loss in mg/dm². The maximum loss for an acid-resistant glass belonging to acid class 1 is 0.70 mg/dm². The maximum loss for a glass belonging to acid class 2 is 1.5 mg/dm². The maximum loss for acid class 3 is 15 mg/dm².

[0066] The alkali resistance L in accordance with DIN ISO 695. The table in each case indicates the weight loss in mg/dm². The maximum loss for a glass belonging to alkali class 1 (weakly soluble in alkaline solutions) is 75 mg/dm². The maximum loss for a glass belonging to alkali class 2 is 175 mg/dm². TABLE I COMPOSITIONS (in % by weight, based on oxide) OF EXEMPLARY EMBODIMENTS (A1-A2) AND COMPARATIVE EXAMPLES (V1-V4) AND THEIR MAIN PROPERTIES A1 A2 A3 A4 A5 A6 A7 A8 SiO₂ 73.0 69.5 73.5 68.6 76.5 63.6 63.1 65.0 B₂O₃ 10.8 9.5 17.0 17.5 13.7 17.5 17.5 16.5 Al₂O₃ — — — — — — — — Li₂O 0.3 0.4 0.15 0.7 0.2 0.7 0.7 0.7 Na₂O 1.7 2.0 0.1 0.90 0.3 0.9 0.9 1.6 K₂O 8.8 9.5 6.2 8.7 4.8 8.7 8.7 7.7 MgO — — — — — — — — CaO — — 0.90 — — — — — BaO — — 0.65 — — — — — ZnO — — — 0.8 — 0.8 0.8 1.5 TiO₂ — — 0.5 — — 4.9 5.4 4.9 ZrO₂ 5.4 9.0 1.0 2.8 4.5 2.8 2.8 2.0 α[10⁻⁶/K]* 5.10 5.25 3.95 5.10 3.30 5.09 5.17 5.12 T_(g)[° C.] 560 560 535 505 525 503 506 501 E_(w)[° C.] n.d. n.d. 785 725 n.d. n.d. n.d. n.d. V_(A)[° C.] 1170 1180 1155 1060 1270 1012 1002 1012 H[μg/g of Na₂O] 9 8 140 110 8 n.d. n.d. n.d. S[mg/dm²] 0.5 0.5 2.8 3.3 n.d. n.d. n.d. n.d. L[mg/dm²] 44 28 130 105 n.d. n.d. n.d. n.d. UV blocking n.d. n.d. n.d. n.d. n.d. 303 305 303 [nm] A9 A10 A11 V1 V2 V3 V4 SiO₂ 65.5 65.5 65.0 72.7 75.5 69 81.0 B₂O₃ 16.5 16.5 16.5 10.0 16.5 18.5 12.0 Al₂O₃ — — — 6.1 1.5 3 2.5 Li₂O 0.7 0.7 0.7 — — 0.5 — Na₂O 1.0 1.6 1.0 7.2 4 1 3.5 K₂O 7.7 7.6 7.7 1.3 1.5 7.5 0.6 MgO — — — — 0.5 — — CaO — — — 1.1 0.5 — — BaO — — — 1.6 — — — ZnO 2.0 2.0 2.0 — — 0.5 — TiO₂ 4.9 5.0 6.5 — — — — ZrO₂ 1.5 1.0 1.5 — — — — α[10⁻⁶/K]* 4.95 5.16 5.13 5.50 3.90 4.95 3.30 T_(g)[° C.] 497 500 497 565 525 495 525 E_(w)[° C.] n.d. n.d. n.d. 765 775 720 825 V_(A)[° C.] 1018 999 1010 1150 1135 1055 1260 H[μg/g of Na₂O] n.d. n.d. n.d. 13 190 160 8 S[mg/dm²] n.d. n.d. n.d. 0.6 3.4 20 0.5 L[mg/dm²] n.d. n.d. n.d. 126 215 261 140 UV blocking 306 302 320 n.d. n.d. n.d. n.d. [nm]

[0067] Glass A1 is particularly suitable as pharmaceutical glass, has a better hydrolytic stability than most comparative glasses and for all the chemical resistances fulfills the requirements of the corresponding class 1. The melting point is 1530° C. and is approximately 50° C. lower than that of the comparative glasses.

[0068] Glass A2 is particularly suitable as glass for glass fibers in concrete. It likewise fulfills the requirements of classes 1 for all the chemical resistances and in particular has an excellent alkali resistance. The melting point is 1530° C., corresponding to that of a conventional pharmaceutical glass.

[0069] Glass A3 is particularly suitable as tungsten sealing glass and has better chemical resistances and an improved resistance to devitrification than the comparative glass V2. The melting point of A3 is 1560° C.

[0070] Glass A4 is particularly suitable as a sealing glass for molybdenum and metals of the KOVAR® class and has better chemical resistances than the comparative glass V3.

[0071] Glass A5 is particularly suitable as glass for equipment and apparatus in laboratories and production areas used in the chemical industry. It has a high ability to withstand temperature changes and the same low coefficient of thermal expansion as the comparative glass V4.

[0072] Glasses A6-A11, which have a high TiO₂ content, have very good UV blocking properties. They are therefore particularly suitable as lamp glasses for fluorescent lamps, in particular for miniaturized fluorescent lamps.

[0073] The disclosure in German Patent Application 102 38 930.6-45 of Aug. 24, 2002 is incorporated here by reference. This German Patent Application describes the invention described hereinabove and claimed in the claims appended hereinbelow and provides the basis for a claim of priority for the instant invention under 35 U.S.C. 119.

[0074] While the invention has been illustrated and described as embodied in aluminum-free borosilicate glass and articles made therewith, it is not intended to be limited to the details shown, since various modifications and changes may be made without departing in any way from the spirit of the present invention.

[0075] Without further analysis, the foregoing will so fully reveal the gist of the present invention that others can, by applying current knowledge, readily adapt it for various applications without omitting features that, from the standpoint of prior art, fairly constitute essential characteristics of the generic or specific aspects of this invention.

[0076] What is claimed is new and is set forth in the following appended claims. 

I claim:
 1. Aluminum-free borosilicate glass with chemical resistance and having a composition, in percent by weight, based on oxide content, of: SiO₂ 60-78 B₂O₃  7-20 Li₂O 0-2 Na₂O 0-4 K₂O  3-12 MgO 0-2 CaO 0-2 with MgO + CaO 0-3 BaO 0-3 ZnO 0-2 ZrO₂ 0.8-12  TiO₂  0-10 CeO₂ 0-1 F⁻   0-0.6

and optionally at least one refining agent in a standard amount for refining.
 2. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 67-75 B₂O₃  9-18 Li₂O 0-1 Na₂O 0-3 K₂O  5-10 with Li₂O + Na₂O + K₂O  5.5-13.5 CaO 0-1 BaO 0-1 ZnO 0-1 TiO₂ 0-1 ZrO₂  0.8-10.5 CeO₂   0-0.4 F⁻   0-0.6

and optionally at least one refining agent in a standard amount for refining.
 3. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 68-74 B₂O₃  9-13 Li₂O 0-1 Na₂O 0-3 K₂O  5-10 with Li₂O + Na₂O + K₂O  5.5-13.5 ZrO₂ 3-7 CeO₂   0-0.4 F⁻   0-0.6

and optionally at least one refining agent in a standard amount for refining.
 4. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 71-74 B₂O₃  9-12 Li₂O 0-1 Na₂O 0-3 K₂O  7-10 with Li₂O + Na₂O + K₂O   7-13.5 ZrO₂ 4-7

and optionally at least one refining agent in a standard amount for refining.
 5. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 68-71 B₂O₃  8-11 Li₂O 0-1 Na₂O 0-3 K₂O  8-11 with Li₂O + Na₂O + K₂O   8-13.5 ZrO₂  7.5-10.5

and optionally at least one refining agent in a standard amount for refining.
 6. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 70-75 B₂O₃ 15-18 Li₂O 0-1 Na₂O 0-3 K₂O 5-8 with Li₂O + Na₂O + K₂O  5.5-10.5 CaO 0-1 BaO 0-1 TiO₂ 0-1 ZrO₂ 0.8-5  

and optionally at least one refining agent in a standard amount for refining.
 7. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 67-70 B₂O₃ 15-18 Li₂O 0-1 Na₂O 0-3 K₂O  7-10 with Li₂O + Na₂O + K₂O   7-12.5 ZnO 0-1 ZrO₂ 2.5-6  

and optionally at least one refining agent in a standard amount for refining.
 8. Aluminum-free borosilicate glass as defined in claim 1, characterized by a composition, in percent by weight, based on oxide content, of: SiO₂ 74-78 B₂O₃ 12-15 Li₂O 0-1 Na₂O 0-3 K₂O 3-8 with Li₂O + Na₂O + K₂O  3-11 ZnO 0-1 ZrO₂ 2.5-7  

and optionally at least one refining agent in a standard amount for refining.
 9. Aluminum-free borosilicate glass as defined in claim 1, and containing at least 0.2 percent by weight of said Li₂O.
 10. Aluminum-free borosilicate glass as defined in claim 1, and containing at least 0.3 percent by weight of said Na₂O.
 11. Aluminum-free borosilicate glass as defined in claim 1, and containing at least 0.5 percent by weight of said Na₂O.
 12. Aluminum-free borosilicate glass as defined in claim 1, and containing at least 0.2 percent by weight of said Li₂O and at least 0.3 percent by weight of said Na₂O.
 13. Aluminum-free borosilicate glass as defined in claim 1, free of As₂O₃ and Sb₂O₃ apart from inevitable impurities thereof.
 14. Aluminum-free borosilicate glass as defined in claim 1, having a coefficient of thermal expansion α(20° C.; 300° C.) of between 3.0×10⁻⁶/K and 6×10⁻⁶/K and a working point VA of between 990° C. and 1290° C.
 15. A primary pharmaceutical packaging material consisting of the aluminum-free borosilicate glass as defined in claim
 1. 16. A glass fiber comprising the aluminum-free borosilicate glass as defined in claim
 1. 17. The glass fiber as defined in claim 16, and having a composition and properties for reinforcing concrete.
 18. A sealing glass for tungsten, molybdenum or KOVAR® consisting of the aluminum-free borosilicate glass as defined in claim
 1. 19. A fluorescent lamp made with the aluminum-free borosilicate glass as defined in claim
 1. 20. The fluorescent lamp as defined in claim 19 and consisting of a miniaturized fluorescent lamps.
 21. An apparatus glass consisting of the aluminum-free borosilicate glass as defined in claim
 1. 